Forums/Tutorials/Laser Cutting Tutorials & Tips

How to make interlocking wood designs

Josh Judkins
posted this on March 21, 2011 11:40

What is a node and how do you create a good one?
Advice from Dan Emery - originally posted to the Ponoko Blog.

A node is typically used if your design has multiple parts that need to join together either by slotting or with a tab and hole joint.

Nodes are little bumps located in the slots or on tabs in your product that are there to help compensate for material thickness variations and the laser kerf. This idea is they compress when a product is assembled providing friction at points rather than along the whole surface of the slot. This means the slot can be fractionally wider at the opening allowing the pieces to be slotted together easily but still create a snug joint.

Finding the right balance between easy to put together but tight when assembled is no mean feat and is probably quite subjective. What I find easy to put together, some people don't. It's best to get a few people to have a go putting your design together if you intend to sell it as a flat pack item.

So what is the key for a successful node?

Symmetry - It's best to have nodes on both sides of a slot mirroring each other. This will minimize any potential twisting that might occur if nodes are offset.

Shape - A gentle curve works well. Something that leads on easily but provides good friction when it's on.

Multiple sets - If the length of the slot allows, you can have two or more sets of nodes. Again will minimize any twisting that might want to happen. Have one pair near the start of the slot and one about halfway between the middle and the end of the slot.

Length of the node - The longer the node the gentler the curve which seems to make the pieces easier to slide on and off. The minimum length of the node should be approximately 0.2in or 5mm.

Width of the node - This will depend on the material you are using. If the material is dense, like MDF, and has little compression then the nodes should be shallow about 0.01in or 0.2mm each. So taking into account of nodes on both sides of the slot, that allows for 0.02in or 0.4mm in variation. If the material is less dense, like Eurolite Poplar, and therefore can compress more then you can use a bigger node, 0.02in or 0.5mm. It might pay to test a few different sizes in some mock ups (like the examples below) before committing to your full design to test exactly what will work with the material you wish to use.

This information will work best with the plywood and timbers offered on Ponoko. The timbers tend to be a lot more forgiving when creating interlocking designs whereas Acrylic can be brittle and a bit trickier to work with. I'll go into more detail about plastic joints in a later post.

Below are diagrams of the experiment I did to illustrate the differences in node types with a video showing the physical results.

diagrams.jpgnode-dimensions.jpg

Now this information is to be used as a guide to help you reduce the number of prototypes needed when creating products with Ponoko. It should be used in conjunction with the information on the laser kerf in a previous post to help make a best guess at how to design your joints.

Feel free to be creative with nodes and let us know any successes or failures so we can learn from them.

 

Comments

User photo
Nicole Heipt

Does anyone know the specs for node size on Birch Ply?  This post mentions MDF and poplar, but it seems as though a lot of the interlocking pieces are made of birch ply.  I'm going to be using 3 layer birch ply for my project and will absolutely need to incorporate nodes.  Any advice will be super!

April 12, 2012 15:02
User photo
Annie

very handy info... not sure how I've missed it before. Thanks

June 18, 2012 21:06
User photo
Neil Moloney
I recently made a box from the 5.7mm cherry veneer over MDF. I used a single node on each side of my slots, of 0.1mm which projected into the void. This box went together with no glue and is SOLID! Thanks for the advice!
September 05, 2012 20:21
User photo
Josh Judkins
Ponoko

Awesome Neil! Thanks for the follow-up on your project - it sure is satisfying when parts snap together like that.

Cheers!

September 07, 2012 11:33
User photo
putyn

could this be used on acrylic parts too ? 

November 16, 2013 08:44